http://hdl.handle.net/20.500.12128/11257| Tytuł: | Corrosion properties of Ca65-xMg17.5Zn17.5+x (x = 0, 2.5, 5) alloys |
| Autor: | Babilas, R. Wojciechowski, P. Bajorek, Anna Sakiewicz, P. Cesarz-Andraczke, K. |
| Słowa kluczowe: | Ca-based alloys; Corrosion; Hydrogen evaluation; X-ray photoelectron spectroscopy |
| Data wydania: | 2019 |
| Źródło: | Archives of Metallurgy and Materials, 2019, no. 3, s. 1033-1040 |
| Abstrakt: | The aim of the paper is to study the effect of zinc addition on the corrosion behavior of Ca65–xMg17.5Zn17.5+x (x = 0, 2.5, 5 at.%) alloys in simulated physiological fluids at 37°C. The electrochemical measurements allowed to determine a corrosion potential, which showed a positive shift from –1.60 V for Ca65Mg17.5Zn17.5 alloy to –1.58 V for Ca60Mg17.5Zn22.5 alloy, adequately. The more significant decrease of hydrogen evolution was noticed for Ca60Mg17.5Zn22.5 alloy (22.4 ml/cm2) than for Ca62.5Mg17.5Zn20 and Ca65Mg17.5Zn17.5 samples (29.9 ml/cm2 and 46.4 ml/cm2), consequently. The corrosion products after immersion tests in Ringer’s solution during 1 h were identified by X-ray diffraction and X-ray photoelectron spectroscopy as calcium, magnesium oxides, carbonates, hydroxides and calcium hydrate. |
| URI: | http://hdl.handle.net/20.500.12128/11257 |
| DOI: | 10.24425/amm.2019.129492 |
| ISSN: | 1733-3490 |
| Pojawia się w kolekcji: | Artykuły (WNŚiT) |
Pliki tej pozycji:
| Plik | Opis | Rozmiar | Format | |
|---|---|---|---|---|
| Babilas_Corrosion_properties.pdf | 5,06 MB | Adobe PDF | Przejrzyj / Otwórz |
Uznanie autorstwa - użycie niekomercyjne 3.0 Polska Creative Commons