http://hdl.handle.net/20.500.12128/9434| Tytuł: | Martensitic transformation in NiTi alloy covered by protective multi-layers |
| Autor: | Goryczka, Tomasz Dudek, Karolina Lelątko, Józef Wierzchoń, T. |
| Słowa kluczowe: | Martensitic transformation; NiTi; protective layer; TiO2 TiN; hydroxyapatite |
| Data wydania: | 2015 |
| Źródło: | "Materials Today: Proceedings" Vol. 2, Suppl. 3 (2015), s. 779-883 |
| Abstrakt: | Commercial NiTi shape memory alloy was covered with multi-layers. First, titanium nitride and titanium oxide was deposited on polished surface of the NiTi alloy. Layers were deposited in one process - a glow discharge technique. Second, on the top of the TiN/TiO2 layer the hydroxyapatite (HAp) was deposited using electrophoresis. The HAp layer was sintered at temperature from 5000C up to 9000C for 5 minutes. Influence of the thermal treatments, realized during processing stages, on a course of the martensitic transformation was studied using differential scanning calorymetry (DSC). |
| URI: | http://hdl.handle.net/20.500.12128/9434 |
| ISSN: | 2214-7853 |
| Pojawia się w kolekcji: | Artykuły (WNŚiT) |
Pliki tej pozycji:
| Plik | Opis | Rozmiar | Format | |
|---|---|---|---|---|
| Goryczka_Dudek_martensitic_transformation_in_niti.pdf | 625,26 kB | Adobe PDF | Przejrzyj / Otwórz |
Uznanie autorstwa - użycie niekomercyjne, bez utworów zależnych 3.0 Polska Creative Commons