Tytuł: | Influence of crystallographic orientation on creep resistance of single-crystal superalloy |
Autor: | Kościelniak, Barbara Gancarczyk, Kamil Poręba, Marek Albrecht, Robert |
Słowa kluczowe: | CMSX-4 superalloy; creep resistance; crystal orientation; microstructure |
Data wydania: | 2020 |
Źródło: | "Advances in Manufacturing Science and Technology" (2020), nr 3, s. 93-98 |
Abstrakt: | This paper focuses on the influence of crystallographic orientation on creep resistance of CMSX-4 nickel-based superalloy. The single-crystal rods of CMSX-4 superalloy were manufactured with the use of the Bridgman method at a withdrawal rate of 3 mm/min. The crystallographic orientation of the rods was determined by the X-ray Ω-scan method with OD-EFG diffractometer and the Laue back-reflection technique. The creep tests were performed at a temperature of 982°C and the value of stress σ = 248 MPa. Microstructural investigation before and after the creep test of CMSX-4 superalloy was performed using a scanning electron microscope. The results showed that the distribution of the values of α angle strongly affects the creep resistance of a single-crystal superalloy. |
URI: | http://hdl.handle.net/20.500.12128/17342 |
DOI: | 10.2478/amst-2019-0017 |
ISSN: | 2300-2565 |
Pojawia się w kolekcji: | Artykuły (WNŚiT) |
Plik | Opis | Rozmiar | Format | |
---|---|---|---|---|
Koscielniak_Albrecht_influence_of_crystallographic_orientation.pdf | 4,72 MB | Adobe PDF | Przejrzyj / Otwórz |
Uznanie autorstwa - użycie niekomercyjne, bez utworów zależnych 3.0 Polska Creative Commons