Characteristics of the Mg-Zn-Ca-Gd alloy after mechanical alloying

Abstract

Magnesium-based materials are interesting alternatives for medical implants, as they have promising mechanical and biological properties. Thanks to them, it is possible to create biodegradable materials for medical application, which would reduce both costs and time of treatment. Magnesium as the sole material, however, it is not enough to support this function. It is important to determine proper alloying elements and methods. A viable method for creating such alloys is mechanical alloying, which can be used to design the structure and properties for proper roles. Mechanical alloying is highly influenced by the milling time of the alloy, as the time of the process affects many properties of the milled powders. X-ray diffraction (XRD) and scanning electron microscopy (SEM) with energy-dispersive spectroscopy (EDS) were carried out to study the powder morphology and chemical composition of Mg65Zn30Ca4Gd1 powders. Moreover, the powder size was assessed by granulometric method and the Vickers hardness test was used for microhardness testing. The samples were milled for 6 min, 13, 20, 30, 40, and 70 h. The hardness correlated with the particle size of the samples. After 30 h of milling time, the average value of hardness was equal to 168 HV and it was lower after 13 (333 HV), 20 (273 HV), 40 (329 HV), and 70 (314 HV) h. The powder particles average size increased after 13 (31 m) h of milling time, up to 30 (45–49 m) hours, and then sharply decreased after 40 (28 m) and 70 (12 m) h.