Mechanical properties of Ni-Fe-Cu-P-B alloy produced by two component melt spinning (TCMS)

Abstract

The aim of this work was to investigate the microstructure and mechanical properties of the two-component melt-spun (TCMS) alloy produced from Ni40Fe40B20 and Ni70Cu10P20 melts. The Ni40Fe40B20, Ni70Cu10P20, Ni55Fe20Cu5P10B10 alloys were arc-melted. Then the alloys were melt-spun in the two different ways i.e.: by casting from a single-chamber crucible and from the two-chamber crucible. All of the above mentioned alloys were processed in the first way and the Ni40Fe40B20 and Ni70Cu10P20 were simultaneously cast on the copper roller from the two-chamber crucible. The microstructure of the alloy was studied using transmission electron microscopy (TEM), scanning electron microscopy (SEM) with energy dispersive spectrometry (EDS) and light microscopy. The mechanical properties were investigated using tensile testing and nanoindentation. The two-component melt-spun (TCMS) amorphous Ni55Fe20Cu5P10B10 alloy present hardness, tensile strength and Young modulus on the significantly higher level than for a single phase amorphous Ni55Fe20Cu5P10B10 alloy and slightly below the corresponding values for the Ni40Fe40B20.