Near-IR Luminescence of Rare-Earth Ions (Er3+, Pr3+, Ho3+, Tm3+) in Titanate-Germanate Glasses under Excitation of Yb3+

Abstract

Inorganic glasses co-doped with rare-earth ions have a key potential application value in the field of optical communications. In this paper, we have fabricated and then characterized multicomponent TiO2-modified germanate glasses co-doped with Yb3+/Ln3+ (Ln = Pr, Er, Tm, Ho) with excellent spectroscopic properties. Glass systems were directly excited at 980 nm (the 2F7/2 → 2F5/2 transition of Yb3+). We demonstrated that the introduction of TiO2 is a promising option to significantly enhance the main near-infrared luminescence bands located at the optical telecommunication window at 1.3 μm (Pr3+: 1G4 → 3H5), 1.5 μm (Er3+: 4I13/2 → 4I15/2), 1.8 μm (Tm3+: 3F4 → 3H6) and 2.0 μm (Ho3+: 5I7 → 7I8). Based on the lifetime values, the energy transfer efficiencies (ηET) were estimated. The values of ηET are changed from 31% for Yb3+/Ho3+ glass to nearly 53% for Yb3+/Pr3+ glass. The investigations show that obtained titanate–germanate glass is an interesting type of special glasses integrating luminescence properties and spectroscopic parameters, which may be a promising candidate for application in laser sources emitting radiation and broadband tunable amplifiers operating in the near-infrared range.