dc.contributor.authorChrobak, Artur-
dc.contributor.authorZiółkowski, Grzegorz-
dc.contributor.authorHaneczok, Grzegorz-
dc.identifier.citationActa Physica Polonica A, Vol. 126, nr 1 (2014), s. 178-179pl_PL
dc.description.abstractThe paper refers to magnetic properties of the (Fe80Nb6B14)1􀀀xTbx (x = 0:06 and x = 0:08) bulk nanocrystalline alloys prepared using the vacuum suction casting technique. The samples were in the form of rods with diameters of d = 1:5 mm, 1 mm and 0.5 mm. It was shown that for the alloys with x = 0:08 the signi cant magnetic hardening with the decrease of sample diameter was observed. For d = 0:5 mm the coercive eld equals 2.46 T and the maximum energy product jJHjmax = 77:2 kJ/m3.pl_PL
dc.rightsUznanie autorstwa-Użycie niekomercyjne-Bez utworów zależnych 3.0 Polska*
dc.subjectinżynieria materiałowapl_PL
dc.subjectmateriały nanokrystalicznepl_PL
dc.subjectkrzywe namagnesowaniapl_PL
dc.subjectefekt Mössbauerapl_PL
dc.titleInfluence of cooling rate on magnetic properties of (Fe80Nb6B14)(1-x)Tb-x type of bulk nanocrystalline alloyspl_PL
Appears in Collections:Artykuły (WNŚiT)

Files in This Item:
File Description SizeFormat 
Chrobak_Influence_of_cooling_rate_on_magnetic.pdf691,95 kBAdobe PDFView/Open
Show simple item record

Uznanie autorstwa - użycie niekomercyjne, bez utworów zależnych 3.0 Polska Creative Commons License Creative Commons