Tytuł: | Charakterystyki tribologiczne warstwy Al2O3 modyfikowanej grafitem w skojarzeniu ślizgowym z kompozytami polimerowymi |
Tytuł równoległy: | Tribological characteristics of a graphite modified AL2O3 coating in sliding contact with polymer composites |
Autor: | Bara, Marek Skoneczny, Władysław Kaptacz, Sławomir |
Słowa kluczowe: | oxide coating; composite coating; plastic; tribological properties |
Data wydania: | 2009 |
Źródło: | Tribologia, Nr 4 (2009), s. 23-33 |
Abstrakt: | The paper presents the tribological properties of Al2O3 coatings modified using graphite in a sliding contact with polymer composites. Ceramic-graphite upper surface layers formed on the aluminium alloy EN-AW-5251 using the duplex technology as well as a direct technology were subjected to a contact with the following materials: PEEK, PEEK/BG and T5W, on a T-17 tester under technically dry friction conditions. The tests were carried out at a constant unit pressure of 0.5 MPa and at a constant average sliding speed of 0.2 m/s for all the investigated couples. The tests were carried out along a 6 km distance in four stages, after which the polymer wear was measured. The analysis of the tribological test results has shown a significant reduction of the friction forces and material wear being the result of a modification of the oxide coatings. It has been also found that a modification of polymers with graphite and carbon has a positive impact on their tribological properties, which conditions their application in unlubricated kinematic couples. |
URI: | http://hdl.handle.net/20.500.12128/19714 |
ISSN: | 0208-7774 1732-422X |
Pojawia się w kolekcji: | Artykuły (WNŚiT) |
Plik | Opis | Rozmiar | Format | |
---|---|---|---|---|
Bara_Charakterystyki_tribologiczne.pdf | 885,79 kB | Adobe PDF | Przejrzyj / Otwórz |
Uznanie autorstwa na tych samych warunkach 3.0 Polska Creative Commons