Title: | X-Ray diffraction, mossbauer spectroscopy, and magnetoelectric effect studies of multiferroic Bi5Ti3FeO15 ceramics |
Authors: | Pikula, T. Guzdek, P. Dzik, Jolanta Lisińska-Czekaj, Agata Jartych, E. |
Keywords: | materiały; właściwości magnetyczne; urządzenia elektroniczne; mikroelektronika; promieniowanie rentgenowskie; efekt Mössbauera; spektroskopia |
Issue Date: | 2015 |
Citation: | Acta Physica Polonica A, Vol. 127, nr 2 (2015), s. 296-299 |
Abstract: | Bi5Ti3FeO15 ceramics belongs to multiferroic class of materials. In this work it was prepared by solidstate sintering method and investigated by X-ray di raction, Mössbauer spectroscopy, and magnetoelectric effect measurements. As it was proved by X-ray di raction studies the single-phase Bi5Ti3FeO15 compound was obtained. The Mössbauer investigations revealed paramagnetic character of the compound at room temperature as well as at 80 K. Magnetoelectric measurements were carried out at room temperature using lock-in dynamic method and they proved presence of magnetoelectric coupling in this material. Additional magnetoelectric studies were carried out after subsequent electric poling of the sample. It was found that the maximum value of the coupling coe cient was almost twice bigger than in the case without the initial poling and reached a value of ME 20.7 mV cm1 Oe1. |
URI: | http://hdl.handle.net/20.500.12128/7933 |
DOI: | 10.12693/APhysPolA.127.296 |
ISSN: | 0587-4246 |
Appears in Collections: | Artykuły (WNŚiT) |
File | Description | Size | Format | |
---|---|---|---|---|
Pikula_X_Ray_diffraction_mossbauer_spectroscopy.pdf | 1,1 MB | Adobe PDF | View/Open |
Uznanie autorstwa - użycie niekomercyjne, bez utworów zależnych 3.0 Polska Creative Commons License